Products introduction
Titanium dioxide, strontium oxide and aluminum oxide as the base material, synthetic fibre is synthesized white soft cotton fibre under high temperature and high pressure. It has features of high length to diameter ratio, high temperature resistance,high modulus, zero shot and easy to disperse. It is applied to high end friction and sealing material.
Technical date
| Appearance | Whiteness | Purity | Loss on Ignition | Mosh Hardness | Specific Surface Area | Heat Resistance |
| White Cotton Fibre | >=99% | >=99% | <=0.1% | 3 | 0.3m3/g | 1200℃ |
| Specific Gravity | Bulk density | Diameter | Length | Length to Diameter Ratio | Strength in Tension | Modulus in Tension |
| 0.36±0.05g/cm3 | 0.21±0.05g/cm3 | 4-8μm | 0.5-1.5mm | 60-200 | 22GPa | 196GPa |
| Chemical Composition | TiO+SrO2+SiO2+Al2O3+CaO+MgO+K2O+Na2O | |||||